Product Details:
1. Application
It is applicable for the bunding and packing of wood, paper, cotton spinning, glass, stone, steel, weld tube and all kinds of heavy goods.
2. Features
Surface waxed and edges deburred, high strength and low elongation
3. Finish
Waxed
4. Packing
Standard exporting packing with edge protector, steel hoop and seals, or as per customers requirements.
5. Mechanical property
|
Grade |
Tensile strength Rm （ MPa ） |
Elongation A （ % ） | |
|
Low Intensity Strength |
I |
590 |
5 |
|
II |
685 |
5 | |
|
moderately strong |
III |
735 |
5 |
|
IV |
785 |
6 | |
|
High Tensile |
V |
880 |
7 |
|
VI |
930 |
8 | |
|
VII |
980 |
12 | |
|
Super-high strength |
VIII |
1250 |
6 |
|
Thickness deviation | ||
|
nominal thickness mm |
deviation mm | |
|
general precision (P) |
Higher accuracy (H) | |
|
≤ 0.40 |
± 0.020 |
± 0.015 |
|
＞0.40～0.70 |
± 0.025 |
± 0.020 |
|
＞0.70～1.30 |
± 0.035 |
± 0.025 |
|
＞1.30～1.65 |
± 0.040 |
± 0.035 |
|
Width deviation | |
|
nominal width mm |
deviation mm |
|
≤ 31.75 |
± 0.10 |
|
＞ 31.75 |
± 0.13 |
6. Specification
|
Steel Band Specification Material: KDG | |||||
|
Thickness mm |
Width mm |
Thickness mm |
Width mm |
Thickness mm |
Width mm |
|
0.25 |
8.00 |
0.25 |
9.50 |
0.25 |
12.70 |
|
0.30 |
8.00 |
0.30 |
9.50 |
0.30 |
8.00 |
|
0.36 |
8.00 |
0.36 |
9.50 |
0.36 |
8.00 |
|
0.40 |
9.50 |
0.40 |
12.70 |
0.40 |
16.00 |
|
0.45 |
9.50 |
0.45 |
12.70 |
0.45 |
16.00 |
|
0.45 |
19.00 |
0.50 |
9.50 |
0.50 |
12.70 |
|
0.50 |
16.00 |
0.50 |
19.00 |
0.56 |
12.70 |
|
0.56 |
16.00 |
0.56 |
19.00 |
0.60 |
16.00 |
|
0.60 |
19.00 |
0.60 |
25.00 |
0.70 |
19.00 |
|
0.70 |
25.00 |
0.80 |
19.00 |
0.80 |
25.00 |
|
0.80 |
31.75 |
0.90 |
19.00 |
0.90 |
25.00 |
|
0.90 |
31.75 |
1.00 |
19.00 |
1.00 |
25.00 |
|
1.00 |
31.75 |
1.00 |
40.00 |
1.00 |
51.00 |
|
1.12 |
19.00 |
1.12 |
25.00 |
1.12 |
31.75 |
|
1.12 |
40.00 |
1.12 |
51.00 |
1.26 |
31.75 |
|
1.26 |
40.00 |
1.26 |
51.00 |
1.50 |
31.75 |
|
1.50 |
40.00 |
1.50 |
51.00 |
1.65 |
40.00 |
|
Size can be customized according to your specification | |||||